Insulation board with improved performance

ABSTRACT

An insulation board assembly, having: a foam insulation board; a top facer attached onto a top side of the foam insulation board, the top facer being made of woven material; and a bottom facer attached onto a bottom side of the foam insulation board, the bottom facer being made of woven material. The top and bottom woven facers may have upper and lower coatings and non-woven layers on either side and woven and non-woven layers may be held together with a tie layer.

RELATED APPLICATIONS

The present application claims priority to U.S. Provisional PatentApplication Ser. No. 62/749,530, filed Oct. 23, 2018, entitledInsulation Board Having Woven Facers, and to U.S. Provisional PatentApplication Ser. No. 62/819,089, filed Mar. 15, 2019, entitledInsulation Board With Improved Performance, the entire disclosures ofwhich are incorporated herein by reference in their entireties for allpurposes.

TECHNICAL FIELD

The present invention relates to improved insulation board performanceimparted by enhanced physical properties through the use of woven matsas facers for insulation boards used in building construction in generaland in roofing construction in particular. When used in a roof assembly,the present invention permits the roofing system to meet the Very SevereHail (VSH) testing rating with a low or typical density insulationboard.

BACKGROUND OF THE INVENTION

Currently, facers for polyurethane or polyisocyanurate (Polyiso) foamroofing insulation boards are typically made either from a GlassReinforced Felt (GRF) facer or from a Coated Glass Facer (CGF) material.Facers serve a few purposes on the insulation board and in the roofsystem. For example, facers help provide structural integrity to thefoam board and protect the friable foam surface from forces exerted byhail, foot traffic, heavy HVAC equipment and construction equipment.Facers also provide added strength to the foam board with regard to winduplift performance. Both GRF and CGF contain fiberglass and thus areskin irritants during the manufacturing process and in end-useapplication. With GRF facers, glass fibers are added to the paper toimprove dimensional stability, especially when the facer is wet.However, the glass fibers do not prevent the board from warping due todimensional change in the GRF facer after exposure to moisture, or fromlosing strength while exposed to moisture, such as a leak. While coatedglass facers do offer improved resistance to moisture and mold whencompared to GRF facers, these facers discolor after exposure tomoisture, and are rigid so they do not spread force across the board,and also have the tendency to absorb excessive amounts of chemicalsduring the production of the foam board. Additional disadvantages ofthese fiberglass containing facer materials include: (a) they do notoffer sufficiently strong indentation resistance, (b) they tend to peeloff and delaminate from the polyurethane or polyisocyanurate insulationboards, and (c) the glass fiber content results in handling complaintsduring production and installation of the boards.

Importantly, the fasteners that secure these foam roofing boards to theroof also pass through the boards' facers. Unfortunately, wind upliftacross the boards can cause fastener pull-through which results infailure of the fully adhered roof system. To improve wind upliftperformance of the roof system, additional fasteners are typicallydriven through the insulation board to keep the board anchored to theroof deck.

Therefore, what is instead desired is a polyurethane or polyisocyanuratefoam roofing insulation board facer material that would both provideload spreading and added surface strength. Specifically, it would bedesirable to provide a facer that assists in spreading surface loadssuch that the potential for fastener pull-through during wind uplift canbe reduced or eliminated. The advantage of load spreading to preventfastener pull-through also helps to firmly secure the foam insulationboard to the roof. Another advantage of such added surface strength isthat it would offer increased indentation resistance. This indentationresistance would be advantageous against hail hitting the roof. Mostpreferably, the ideal roofing system would be able to pass the recentlyannounced “Very Severe Hail” test rating announced by Factory Mutual asdescribed in FM 4470 (Class 1—VSH). In addition, a facer having thedesired indentation resistance would also be advantageous againstworkers kneeling on the roof or foot traffic on the roof duringinstallation or roof repair. As will be explained, the present systemprovides this strength and load-spreading advantages. In fact, thepresent system has been shown to meet the Very Severe Hail (VSH) testrating. In addition, the present facer even preferably permits theroofing system to meet the Very Severe Hail (VSH) test rating even whena low or typical density insulation board is used (For example, such adensity range can even be as low as found in typical density insulationboards, and could even be in the range of 0.5 to 6.0 pcf).

While load spreading will allow higher wind uplift values to be achievedwith equivalent fasteners, load spreading will also allow an equivalentuplift to be achieved utilizing fewer fasteners. Reducing the number offasteners in a roof system while maintaining wind uplift performance ishighly advantageous because it requires less labor to install a roofsystem with fewer fasteners, fewer fasteners reduces the material costof the roof system, and fewer fasteners results in fewer penetrations ofthe polyurethane or polyisocyanurate foam board, minimizing heat sinks,thereby leading to improved insulating performance of the insulationboard.

SUMMARY OF THE INVENTION

In one aspect, the present invention comprises an insulation boardassembly, having: a foam insulation board (which may optionally bepolyurethane or polyisocyanurate, or a phenolic material or an expandedpolystyrene material (EPS)); a woven mat as the top facer attached ontoa top side of the foam insulation board; and a woven mat as the bottomfacer attached onto a bottom side of the foam insulation board.Optionally, the woven facers may be made of natural and/or syntheticyarns and/or tapes. Suitable synthetic yarns or tapes can be made frompolymers such as polyethylene, ethylene and alpha-olefin copolymers,polypropylene, propylene and alpha-olefin copolymers, nylon, polyester,acrylic polyester, polyamide, aramid etc. Suitable natural yarns can bemade from nature fibers, such as cotton, cellulose, wool, rayon, silk,hemp, sisal, etc.

The woven mats can have different weave density. Fabric Mesh is ameasure of the density of the fabric weave as the number of yarns ortapes per inch in both the Warp (machine) and Weft (cross) directions.Ends per inch (EPI) is the number of warp yarns or tapes per inch ofwoven fabric and picks per inch (PPI) is the number of weft yarns andtapes per inch of woven fabric. For example, the weave density can be 2tapes per inch×2 tapes per inch (EPI×PPI) to 100 tapes per inch×100tapes per inch. Preferably, the weave density would be 4×4 to 60×60mesh. Most preferably, the weave density would be 4×4 to 30×30 mesh.Optionally, the woven mats have different weave density along warp andweft direction, for example, the weave density can optionally be 4×8mesh in one embodiment.

The present woven mats can have different weights, typically measured bythe fabric weight in ounces per square yard or grams per square meters.For example, the woven mat weight can optionally be from 10 gsm to 400gsm. Preferably, the woven mat weight could be from 20 gsm to 200 gsm.Most preferably, the woven mat weight could be from 40 gsm to 100 gsm.Alternatively, the woven mats can have different thicknesses. Forexample, the woven mat thickness can be from 1 mil to 200 mil.Preferably, the woven mat thickness could be from 2 mil to 100 mil. Mostpreferably, the woven mat thickness could be from 2 mil to 50 mil.

Optionally, the woven mat can have a coating on one or both sides of thesurface. The coating can be of different polymer compositions, such aspolyethylene, ethylene and alpha-olefin copolymers, polypropylene,propylene and alpha-olefin copolymers, silicones, acrylates, naturalrubber, styrene-butadiene rubber, etc. Advantageously, such coating willprovide bleed through resistance during the polyurethane orpolyisocyanurate board manufacturing process, water resistance duringfoam board transportation, and slip and water resistance during fieldinstallation. The coating may additionally provide improved adhesion tothe polyurethane or polyisocyanurate foam during manufacturing andprovide improved compatibility and adhesion to bonding adhesives duringfield installation. The bonding adhesives can consist of differentpolymer compositions, such as polyurethane, nitrile, neoprene,chloroprene, silane-terminated polyether, styrene butadiene rubber,acrylic, ethylene propylene diene monomer (EPDM), etc.

Optionally, each of the top and bottom woven mats can have an additionallayer of non-woven material laminated to one or both sides. Thelamination could optionally be done with adhesives or with a tie layer.When the non-woven layer is in contact with the polyurethane orpolyisocyanurate insulating foam during the manufacturing process, thenon-woven layer may increase the surface roughness and surface area ofthe woven mat to allow the woven mat to have better adhesion or bondingwith the polyurethane or polyisocyanurate foam. When the non-woven layeris positioned on the outside (i.e.: top or bottom) of the foaminsulation board, it may enhance the slip resistance and improveadhesion performance with bonding adhesives during the fieldinstallation. The non-woven fiber can optionally be made of differentpolymer composition, such as polyester, polyethylene, ethylene andalpha-olefin copolymers, polypropylene, propylene and alpha-olefincopolymers, nylon, glass, Kevlar, basalt, carbon fiber, etc.

Optionally, the woven mats may be laminated with a glass scrim, glassmat, carbon fibers scrim, or coated PET scrim. When laminated to thewoven mat, these materials could potentially improve dimensionalstability of the facer and the insulation board.

Optionally, the woven mats can be made of low shrinkage polymer yarns ortapes. The shrinkage rate of polymer tape can be assessed by thepercentage of length change when the polymer tape is heated from roomtemperature to 100° C. Preferably, the polymer tape used in the wovenmat has <10% in shrinkage rate. Most preferable, the polymer tape has<5% shrinkage rate.

Optionally, flame retardants can be added to polymer yarns or tapes toenhance the fire resistance of the woven facer.

In another aspect, the present invention comprises a rolled woven facermaterial having a sufficiently desirable strength in both its machinedirection and its cross direction. This rolled woven material can thenbe used as a top and/or bottom facer to a polyurethane orpolyisocyanurate foam insulation board. Preferably, this rolled wovenfacer material is quite thin and has low weight.

In preferred embodiments, the present woven polypropylene facer has atensile strength greater than 80 lbf/3 inch in both a machine directionand a cross direction, and also has a tongue tear strength of over 15lbf in both a machine direction and a cross direction.

Advantages of the present woven facer material include the fact that itprovides added surface strength, load-spreading and durability ascompared to existing GRF and CGF facers. Such added surface strength andload-spreading allows for foot traffic and kneeling on the insulationboards during roof installation. It also provides superior hailresistance and equivalent mold/moisture resistance to that of CGF.Specifically, the present roofing system comprising the present facerhas been shown to meet the “Very Severe Hail” test rating announced byFactory Mutual as described in FM 4470 (Class 1—VSH).

The present woven facer is preferably a light but strong and heavy dutymaterial. An advantage of the present woven facer material is that ithas higher fastener pull through force, and thus provides excellent winduplift resistance after the insulation board has been secured to theroof. In addition, the present woven facer system is also very durableand lengthens the effective lifespan of the foam roofing insulationboard. In optional embodiments, the woven facers are made of a polymer,such as polyethylene, ethylene and alpha-olefin copolymers,polypropylene, propylene and alpha-olefin copolymers, nylon, polyester,polyamide, etc. However, it is to be understood that other wovenmaterials including both natural and synthetic yarns or tapes, such ascotton, cellulose, rayon, silk, hemp, sisal, etc. can be used as well.

As such, the present woven facer system also offers the advantages of ahigher flex modulus and a higher fastener-plate pull-through resistanceas compared to traditional GRF and CGF facers.

In the case of a woven polypropylene material, the present facer canoptionally be made from a plastic film that has been drawn intofilaments or tapes, and then woven to create a fabric sheet or mat. Inthese preferred aspects, the woven mat optionally comprises a nonwovenlayer on one side that will promote adhesion to the polyurethane orpolyisocyanurate foam and polymer coating on the other side that willenhance water, moisture and bleed through resistance. The polymercoating can optionally provide improved compatibility and adhesion tobonding adhesives during field installation.

Another advantage of the present woven facer material is its low cost.In addition, the present woven facer materials can optionally be madefrom recycled plastics, providing environmental benefits.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional side elevation view of a foam insulation boardwith top and bottom woven facers.

FIG. 2 is a sectional side elevation view of a foam insulation boardsimilar to FIG. 1, but with a non-woven layer or coating above and beloweach of the top and bottom woven facers.

FIG. 3 is a sectional side elevation view of a foam insulation boardsimilar to FIG. 2, but with a tie layer securing the woven and non-wovenlayers together.

DETAILED DESCRIPTION OF THE PRESENT SYSTEM

As stated above, in one embodiment as seen in FIG. 1, the present systemprovides an insulation board assembly 10 that comprises: a foaminsulation board 12 that may optionally be made of polyurethane orpolyisocyanurate foam, or a phenolic material or an expanded polystyrenematerial (EPS)); a top woven facer 20A attached onto a top side of thefoam insulation board, top facer 20A being made of woven material thatmay optionally include polypropylene; and a woven bottom facer 20Battached onto a bottom side of the foam insulation board, bottom facer20B also optionally being made of woven polypropylene. In alternateaspects, other woven materials may be used instead, including bothnatural and synthetic fibers.

In another embodiment, the present system provides a thin, rolled wovenfacer material that has sufficient strength in both its machine andcross directions that can be attached onto the foam insulation board(for example, during an extrusion process with the foam being sandwichedbetween top and bottom woven facers).

Traditionally, polyurethane or polyisocyanurate is a closed-cell, rigidfoam insulation board consisting of a foam core sandwiched between twofacers. It is the most widely used insulating material for above-deckcommercial roof construction in North America. In many existing systems,the facer materials are fiberglass, but even kraft paper has been used.These polyurethane or polyisocyanurate insulation boards are attached tothe roof deck with various mechanical fasteners and constructionadhesives or held in place with ballast stones or concrete pavers placedabove the roofing membrane. Typically, the roofing membrane also may bemechanically attached through the foam insulation, adhered to the toppolyurethane or polyisocyanurate facer or even held in place withballast.

In accordance with the present system, the present inventorsexperimentally tested various facers (GRF, CGF, Non-woven polyester andwoven polypropylene facer materials). The results of these experimentaltests are shown in Table 1, below:

TABLE 1 Common physical properties of different facer materials.Nonwoven Woven GRF CGF PET PP Tensile (MD) (lbf/3 in.) 46 69 107 132Tensile (CD) (lbf/3 in.) 38 67 67 119 Breaking Elongation-MD (%) 1.7 239 14 Breaking Elongation-CD (%) 2 2 50 12 Tear MD (lbf) 0.4 0.6 6.847.0 Tear CD (lbf) 0.7 0.8 10.5 49.0

In addition, the present inventors also experimentally tested the samefacer materials for “Pull-Through” and “wind uplift”. The results ofthese experimental tests are shown in Table 2 below.

The Pull-Through test procedure is designed to evaluate the strength ofsubstrate/stress plate combinations by using tensile loading. The testmethod described below utilizes a nominal 14×14 in. test sample and testjig. The test method is intended to be used to evaluate variousmembranes, membrane/stress plate combinations, substrates orsubstrate/stress plate combinations for comparison to each other inorder to determine the products are to be used large scale windresistance classification testing.

The detailed testing procedure is as follows. The 14×14 Substrate TestJig is secured to the moving crosshead of the Tinius Olsen machine. Whenready for testing, the sample is slid into the 14×14 Substrate Test Jigwith the stress plate located on the underside of the test sample. Thescrew end of the fastener is then secured in into the stationary jaw.Zero the Tinius Olsen machine to clear data before the first sample istested. Force is exerted in a direct line perpendicular to the plane ofthe substrate/stress plate interface at a crosshead speed of 2 in./min(51 mm/min). While the sample is being tested, the sample shall bevisually examined to ensure that it continues to meet the Conditions ofAcceptance. Continue the testing until the sample fails, higher forcesare unable to be attained or maintained, or at the discretion of thetest sponsor. Failure is considered to occur when the Conditions ofAcceptance are no longer being met or until the tensile force is nolonger able to be maintained. Upon completion of the test, the sampleshall be examined and any item not conforming to the Conditions ofAcceptance noted. The results of the Pull-Through Test shall be statedin pounds. The result assigned to the sample shall be the maximum forcewhich the sample reached prior to failure. Conditions of Acceptanceare: 1. all samples should remain secured in their test jig untilfailure of the test sample; 2. the overall sample results shall bedetermined based on the average of three (3) tests. If the standarddeviation of the three values divided by the mean is greater than 20%,an additional test(s) shall be conducted. The results of all tests shallbe used to determine the final average.

TABLE 2 Performance of polyisocyanurate board with different facermaterials. Facer Type GRF CGF Nonwoven PET Woven PP Pull-through (lbf)177 262 263 455 Wind uplift 1-60 1-90 1-105 1-120

While the woven facer performed exceedingly well when compared to GRFand CGF with fastener pull-through/wind uplift, it also shows superiorperformance with regard to moisture resistance per ASTM C209-WaterAbsorption. This is shown below in Table 3.

TABLE 3 Moisture absorption of polyisocyanurate board with differentfacer materials. Facer Type GRF CGF Nonwoven PET Woven PP WaterAbsorption 0.39% 0.30% 0.07% 0.06%

As a result of this testing, it was discovered that woven polypropylenefacers 20A and 20B offered substantial benefits (as described herein)over traditional GRF and CGF facers.

In particular, the present woven facers 20A and 20B provide theadvantages of strength in both (perpendicular) machine direction andcross directions. In preferred aspects, the strength in the crossdirection is at least 70% of the strength in the machine direction.

In the case of woven facer materials supplied on rolls, the presentfacer materials preferably have weight of 20 gsm to 200 gsm; and atensile strength of at least 80 lb. The advantage of this smallthickness is that it makes the facers easier to roll.

In various optional aspects, the woven facers 20A and 20B can be made ofnatural and/or synthetic yarns and/or tapes. The synthetic yarns ortapes can be made from polymers such as polyethylene, ethylene andalpha-olefin copolymers, polypropylene, propylene and alpha-olefincopolymers, nylon, polyester, acrylic polyester, polyamide, aramid etc.The yarns can be made from natural fibers, such as cotton, cellulose,wool, rayon, silk, hemp, sisal, etc.

In preferred embodiments, the present insulation board assembly meetsthe Very Severe Hail (VSH) rating of FM 4470 (Class 1). This can even beaccomplished using low or typical density insulation board. In oneembodiment, the foam insulation board has a density of 0.5 to 6.0 pcf.This represent an advantage over existing (and costlier) approaches ofusing gypsum or press board to achieve the Very Severe Hail (VSH)rating.

In addition, the adhesion between the insulation board and the facercould potentially be stronger than can be achieved by existing standarddensity insulation boards and facers made of paper, glass fiberreinforced paper or coated glass facers (GRF/CGF), foils, films orlaminates.

In optional preferred embodiments, the present insulation board withwoven facer may also be used under a sheet of roof membrane, such asEPDM (Ethylene Propylene Diene Monomer), TPO (thermoplastic olefin), PVC(polyvinyl chloride), KEE (ketone ethylene ester) or Hypalon, of variousthickness to provide a roofing structure capable of achieving the VerySevere Hail (VSH) rating. Optionally, EPDM, TPO, PVC, KEE and Hypalonroof membrane can have non-woven materials laminated on the back side.The non-woven fleece could potentially improve the adhesion performanceof roof membrane to the insulation board.

In other optional preferred aspects, bonding adhesives are used toadhere the roof membrane onto the insulation board. Optionally, suchbonding adhesive can include extruded coatings, spray coatings or rollerapplied coatings. Examples of such adhesive promoters include FlexibleFAST™, TPO bonding adhesive, Cav-Grip III™ and EPDM bonding adhesive.

Roof System Performance:

Factory Mutual's 4470's procedure for Very Severe Hail (VSH) Testing isa new test standard that has had a significant impact on theconstruction of commercial roof systems in fourteen states throughoutthe Midwest. The test involved propelling a 2-inch-diameter ice ball ata roof system test specimen at a velocity of 152 to 160 feet per second.The membrane must not be punctured and it must remain adhered to thesubstrate board. The substrate boards cannot be cracked or have thefacers delaminated from the foam to pass this test.

Two widely used cover boards (i.e.: High Density (HD) Polyiso and Gypsumboard), that are used in the commercial roofing industry have beenunable to withstand this VSH test (See Table 4 and 5 below). The onlyroofing systems that have been able to achieve limited success on theVSH rating so far have incorporated OSB cover boards and Plywood coverboards (See Table 6 below). However, the OSB and Plywood boards havesignificant limitation since they are expensive, heavier than 0.5″ HDPolyiso, and are not able to achieve the same fire ratings that systemscontaining Gypsum or HD Polyiso cover boards.

TABLE 4 VSH test results for ½″ SecurShield HD Polyiso board. ReasonTesting VSH for Insulation Membrane Adhesive Location Results failure ½″145 EPDM Fleece Flex FAST FM Fail Cracks SecurShield 115 EPDM FleeceFlex FAST FM Fail in High 90 mil EPDM EPDM FM Fail HD Density BondingBoard Polyiso 75 mil Sure-Tough EPDM FM Fail Board Bonding 145 WhiteEPDM Flex FAST FM Fail Fleece 115 White EPDM Flex FAST FM Fail Fleece 90mil White EPDM FM Fail EPDM Bonding 135 PVC Fleece Flex FAST FM Fail 115PVC Fleece Flex FAST FM Fail 80 mil PVC PVC FM Fail Bonding 135 TPOFleece Flex FAST FM Fail 115 TPO Fleece Flex FAST FM Fail 80 mil TPO TPOFM Fail Bonding

TABLE 5 VSH test results for ½″ DensDeck Prime board (Gypsum). ReasonTesting VSH for Insulation Membrane Adhesive Location Results failure ½″145 EPDM Fleece Flex FAST FM Fail Loss of DensDeck 115 EPDM Fleece FlexFAST FM Fail Adhesion Prime 90 mil EPDM EPDM FM Fail (gypsum BoardBonding turned to 75 mil Sure-Tough EPDM FM Fail powder Bonding at 145White EPDM Flex FAST FM Fail area of Fleece impact) 115 White EPDM FlexFAST FM Fail Fleece 90 mil White EPDM FM Fail EPDM Bonding 135 PVCFleece Flex FAST FM Fail 115 PVC Fleece Flex FAST FM Fail 80 mil PVC PVCFM Fail Bonding 135 TPO Fleece Flex FAST FM Fail 115 TPO Fleece FlexFAST FM Fail 80 mil TPO TPO FM Fail Bonding

TABLE 6 VSH test results for StormBase (OSB) board. Reason Testing VSHfor Insulation Membrane Adhesive Location Results failure StormBase 145EPDM Fleece Flex FAST FM Fail cracks (OSB) 115 EPDM Fleece Flex FAST FMFail in 90 mil EPDM EPDM FM Fail OSB Bonding 90 mil White EPDM FM FailEPDM Bonding 75 mil Sure-Tough EPDM FM Fail Bonding 115 White EPDM FlexFAST FM Fail Fleece 145 White EPDM Flex FAST FM Pass Fleece 135 PVCFleece Flex FAST FM Fail heat 115 PVC Fleece Flex FAST FM Fail aging 80mil PVC PVC Bonding FM Fail fail 135 TPO Fleece Flex FAST FM Pass 115TPO Fleece Flex FAST FM Pass 80 mil TPO TPO Bonding FM Pass

In contrast to the above existing systems, various embodiments of thepresent invention (i.e.: systems containing high density and normaldensity Polyiso insulation boards made with woven polypropylene facermaterials) showed significant improvement and were able to withstand theVSH Test. The present roof systems successfully passed both internal andFactory Mutual tests due to the unique physical properties provided bythe present woven facers. The results are summarized in the Table 7 and8 below.

As can be appreciated, the present roof systems using standard densityor high density insulation board and woven PP facers can be paired withTPO FleeceBACK, EPDM FleeceBACK, PVC FleeceBACK, KEE FleeceBACK andbareback TPO, EPDM, PVC and KEE HP. These membranes may optionally bebonded with two-part polyurethane adhesive, TPO Bonding adhesives, PVCadhesives, EPDM Bonding Adhesives, water based adhesives, LVOC bondingadhesives and Cav-Grip III. This type of roof system has significantperformance advantageous over that with OSB and plywood board as theinsulation board with woven PP facer delivers higher R-value per inchand is less costly.

TABLE 7 VSH test results for ½″ HD Polyiso board with woven PP facer.Testing VSH Insulation Source Membrane Adhesive Location Results ½″ HDThis 45 mil TPO Cav-Grip III in-house pass Polyiso w/ invention 60 milTPO Cav-Grip III in-house pass Woven PP 90 mil White 90-8-30A in-housepass Facer EPDM 105 EPDM Flex FAST in-house pass Fleece 60 mil TPOCav-Grip III FM pass 80 mil TPO Cav-Grip III FM pass

TABLE 8 VSH test results for normal density Polyiso board with woven PPfacer. Testing VSH Insulation Source Membrane Adhesive Location ResultsStandard This 80 mil TPO Cav-Grip III in-house pass Density invention 90mil White 90-8-30A in-house pass Polyiso EPDM w/Woven 105 EPDM Flex FASTin-house pass PP Facer Fleece 60 mil TPO Cav-Grip III FM pass 80 mil TPOCav-Grip III FM pass

In preferred aspects illustrated in FIG. 2, the woven facers preferablyinclude chemical coatings to make them waterproof. Specifically, system10 comprises a foam insulation board 12, having a top woven facer 20Aand a bottom woven facer 20B, as described above. Preferably, top wovenfacer 20A and bottom woven facer 20B comprise no glass fibers. Foaminsulation board preferably has a density of 0.5 to 6.0 pcf and thefastener Pull-Through value is higher than 300 lbf. Preferably, the roofassembly 10 consists of roof membrane, bonding adhesive and theinsulation board, and wherein the roof assembly meets the Very SevereHail rating of FM 4470 (Class 1).

Preferably, each of woven facers 20A and 20B comprise yarns or tapesmade from synthetic polymers such as woven polypropylene and/orpropylene alpha-olefin copolymers or ethylene alpha-olefin copolymershaving a warp density from 4 to 30 EPI or a weft density from 4 to 30PPI, a weight from 40 to 200 grams per square meter, and a thickness of2 mil to 50 mil. Preferably, each of the top and bottom facers 20A and20B have a tensile strength greater than 80 lbf/3 inch in both a machinedirection and a cross direction and a tear strength of over 15 lbf inboth a machine direction and a cross direction.

As seen in FIG. 2, each of facers 20A and 20B may optionally have apolymer coating on one or both side of one or both of the top and bottomfacers (i.e.: 22A, 24A, 22B and 24B). In preferred aspects, some or allof polymer coating layers 22A, 24A, 22B and 24B are selected from thegroup consisting of: polyethylene, ethylene and alpha-olefin copolymers,polypropylene, propylene and alpha-olefin copolymers, silicones,acrylates, polyurethane, natural rubber, and styrene butadiene rubber.

Alternatively, each of facers 20A and 20B may optionally have anon-woven material laminated on one or both side of one or both of thetop and bottom facers (i.e.: layers 22A, 24A, 22B and 24B). Thenon-woven material layers may be selected from the group consisting ofpolyester, polyethylene, ethylene and alpha-olefin copolymers,polypropylene, propylene and alpha-olefin copolymers, nylon, glass,Kevlar, basalt, and carbon fiber. As such, layers 22A, 24A, 22B and 24Bcan comprise various polymer coatings or other non-woven material.Optionally, layers 24A and 24B can comprise a laminated glass mat, aglass scrim or a coated glass scrim.

Finally, as seen in FIG. 3, the non-woven layers 24A and 24B can belaminated to the woven layers 20A and 20B via an adhesive or a tie layer26A, 26B.

In alternate aspects, the present system comprises a rolled insulationfacer formed from a woven material having a tensile strength greaterthan 80 lbf/3 inch in both a machine direction and a cross direction,and a tear strength of over 15 lbf in both the machine direction and thecross direction. In this aspect, the woven material comprises yarns ortapes made from synthetic polymers, including but not limited topolypropylene and/or propylene alpha-olefin copolymers and/or ethylenealpha-olefin copolymers. Preferably, the woven material is waterproof.

What is claimed is:
 1. An insulation board assembly, comprising: a foaminsulation board having first and second opposing surfaces; a top singlelayer facer attached onto a top side of the foam insulation board,wherein the top single layer facer is in direct contact with the firstsurface of the foam insulation board, the top facer being made of wovenmaterial having a warp density from 4 to 30 ends per inch or a weftdensity from 4 to 30 picks per inch and a tensile strength greater than80 lbf/3 inch in both a machine direction and a cross direction and atear strength of over 15 lbf in both a machine direction and a crossdirection, the top single layer facer defining an outermost top surfaceof the insulation board assembly; and a bottom single layer facerattached onto a bottom side of the foam insulation board, wherein thebottom single layer facer is in direct contact with the second surfaceof the foam insulation board, the bottom facer being made of wovenmaterial having a warp density from 4 to 30 ends per inch or a weftdensity from 4 to 30 picks per inch and a tensile strength greater than80 lbf/3 inch in both a machine direction and a cross direction and atear strength of over 15 lbf in both a machine direction and a crossdirection, the bottom single layer facer defining an outermost bottomsurface of the insulation board assembly, wherein the insulation boardassembly when adhered or mechanically fastened onto a roof assemblypermits the roof assembly to meet the Very Severe Hail rating of FM 4470(Class 1), and wherein the woven material comprises woven polypropyleneand/or propylene alpha-olefin copolymers or ethylene alpha-olefincopolymers.
 2. The insulation board assembly of claim 1, wherein thefoam board is a polyisocyanurate or polyurethane foam board.
 3. Theinsulation board assembly of claim 1, wherein the top facer and thebottom facer comprise no glass fibers.
 4. The insulation board assemblyof claim 1, wherein the foam insulation board has a density of 0.5 to6.0 pcf.
 5. The insulation board assembly of claim 1, wherein theinsulation board assembly exhibits a fastener Pull-Through value that ishigher than 300 lbf.
 6. The assembly of claim 1, wherein the wovenmaterial comprises yarns or tapes.
 7. The assembly of claim 1, whereinthe woven material has a weight from 40 to 200 grams per square meter.8. The assembly of claim 1, wherein the woven material has a thicknessof 2 mil to 50 mil.